EXTRUTEX C-PVC Compound for Industrial Pipe Grade: TG-C610A-G (Deep Grey Powder)
EXTRUTEX C-PVC Compound for Industrial Pipe
Grade: TG-C610A-G (Deep Grey Powder)
Technical Data Sheet
| Property | Unit | Typical Value |
|---|---|---|
| Product Name | — | C-PVC Industrial Pipe Compound |
| Grade | — | TG-C610A-G |
| Appearance | — | Free-flowing Powder |
| Color | — | Deep Grey |
| Base Resin | — | Chlorinated Polyvinyl Chloride |
| Application | — | Industrial Pressure Pipe |
| Recommended Pipe OD | mm | ≥ 600 |
| Vicat Softening Temperature | °C | ≥ 110 |
| Tensile Strength | MPa | ≥ 50 |
| Impact Resistance | kJ/m² | ≥ 10 |
| Density | g/cm³ | 1.50 – 1.65 |
| Heat Stability (200°C) | min | ≥ 30 |
| Processing Temperature | °C | 185 – 210 |
| Melt Fusion Performance | — | Excellent |
| Surface Finish | — | Smooth |
| Dimensional Stability | — | Excellent |
| Chemical Resistance | — | Excellent |
| Pressure Resistance | — | High |
| Weather Resistance | — | Good |
| Extrusion Performance | — | Excellent |
| Moisture Content | % | ≤ 0.30 |
| Packaging | kg/bag | 25 |
EXTRUTEX C-PVC Compound for Industrial Pipe Grade: TG-C610A-G (Deep Grey Powder)
Description
EXTRUTEX C-PVC Compound for Industrial Pipe
Grade: TG-C610A-G (Deep Grey Powder)
Product Description
EXTRUTEX TG-C610A-G is a premium-grade Chlorinated Polyvinyl Chloride (C-PVC) compound developed for the production of large-diameter industrial pressure pipes with outside diameters exceeding 600 mm. The compound is supplied in powder form and engineered to provide excellent heat resistance, long-term hydrostatic strength, superior processability, and outstanding dimensional stability during extrusion.
Its optimized formulation offers enhanced fusion characteristics, smooth melt flow, and excellent mechanical performance required for high-pressure industrial piping systems operating under demanding temperature and chemical exposure conditions. The deep grey color provides a professional industrial appearance while ensuring consistent color uniformity throughout production.
TG-C610A-G is particularly suitable for manufacturing heavy-duty C-PVC pressure pipes used in chemical processing plants, water treatment facilities, industrial fluid transportation systems, mining operations, and corrosive media handling applications.
Key Features
- Premium-grade C-PVC compound
- Designed for pressure pipes with OD ≥ 600 mm
- Excellent hydrostatic pressure resistance
- Superior heat resistance compared with conventional PVC compounds
- Outstanding chemical corrosion resistance
- Excellent fusion and processing stability
- High melt strength for large-diameter pipe extrusion
- Smooth internal and external pipe surface finish
- Low die build-up during processing
- Excellent dimensional stability
- Uniform deep grey coloration
- Long service life under elevated temperatures
- High impact strength and toughness
- Good weathering performance
- Reduced maintenance requirements
- Suitable for industrial and municipal infrastructure projects
Typical Applications
- High-pressure industrial piping systems
- Chemical transportation pipelines
- Water treatment facilities
- Industrial wastewater systems
- Desalination plants
- Mining slurry pipelines
- Process water pipelines
- Cooling water systems
- Corrosive fluid transportation
- Industrial utility piping
- Power plant piping systems
- Municipal infrastructure projects
- Large-diameter pressure pipe production
- Industrial process plants
- Petrochemical support systems
Technical Specification
| Property | Unit | Typical Value |
|---|---|---|
| Product Name | — | C-PVC Industrial Pipe Compound |
| Grade | — | TG-C610A-G |
| Appearance | — | Free-flowing Powder |
| Color | — | Deep Grey |
| Base Resin | — | Chlorinated Polyvinyl Chloride |
| Application | — | Industrial Pressure Pipe |
| Recommended Pipe OD | mm | ≥ 600 |
| Vicat Softening Temperature | °C | ≥ 110 |
| Tensile Strength | MPa | ≥ 50 |
| Impact Resistance | kJ/m² | ≥ 10 |
| Density | g/cm³ | 1.50 – 1.65 |
| Heat Stability (200°C) | min | ≥ 30 |
| Processing Temperature | °C | 185 – 210 |
| Melt Fusion Performance | — | Excellent |
| Surface Finish | — | Smooth |
| Dimensional Stability | — | Excellent |
| Chemical Resistance | — | Excellent |
| Pressure Resistance | — | High |
| Weather Resistance | — | Good |
| Extrusion Performance | — | Excellent |
| Moisture Content | % | ≤ 0.30 |
| Packaging | kg/bag | 25 |
Values shown are typical reference values and may be adjusted according to processing equipment and application requirements.
Processing Recommendations
| Parameter | Recommended Range |
|---|---|
| Material Drying Temperature | 70–80°C |
| Drying Time | 1–2 Hours |
| Barrel Temperature Zone 1 | 175–185°C |
| Barrel Temperature Zone 2 | 180–195°C |
| Barrel Temperature Zone 3 | 185–205°C |
| Die Temperature | 190–210°C |
| Screw Speed | According to pipe dimensions |
| Cooling Method | Vacuum Calibration + Water Cooling |
Advantages of EXTRUTEX TG-C610A-G
- Optimized for large-diameter pipe extrusion
- Consistent processing performance
- Excellent pressure-bearing capability
- Superior thermal resistance
- Long-term durability
- Excellent corrosion protection
- Reduced production downtime
- High production efficiency
- Uniform dispersion and fusion
- Reliable quality for industrial projects
Packaging & Storage
- Packed in 25 kg moisture-resistant bags.
- Store in a cool, dry, and well-ventilated area.
- Protect from direct sunlight and moisture.
- Keep packaging sealed until use.
- Recommended storage temperature below 35°C.
Features of OUR Ca/Zn Stabilizers
These stabilizers carry a quiet brilliance in their chemistry — qualities that make PVC behave not just well, but beautifully. Their strengths unfold like a list of promises:
• Excellent heat stability
They stand firm in the furnace of processing, guarding PVC against the harsh bite of thermal decay. Even under long residence times and high-output conditions, they keep the melt calm, steady, and true.
• Excellent processing
A formulation that flows like a well-rehearsed story — smooth, predictable, effortless. Machines run cleaner, extrusion runs longer, and operators breathe easier.
• High output rates
These stabilizers encourage speed. They let production lines surge forward, pushing greater volumes without sacrificing stability, gloss, or dimensional accuracy.
• Excellent plate-out properties
They keep the metal clean — die lips, barrels, calibrators — all free from waxy buildup. No residue, no streaks, no interruptions. Just pure, disciplined processing.
• Excellent dimensional stability
Pipes and fittings emerge with the confidence of perfect geometry. Sizes remain loyal to standards, resisting distortion, warpage, or shrinkage.
• Excellent surface finish
A stabilizer that leaves behind a sheen — a smooth, glasslike finish that speaks of controlled melt flow and refined lubrication balance.
APPLICATIONS:
Reviews (0)
Reviews
There are no reviews yet.
EXTRUTEX C-PVC Compound for Industrial Pipe
Grade: TG-C610A-G (Deep Grey Powder)
Product Description
EXTRUTEX TG-C610A-G is a premium-grade Chlorinated Polyvinyl Chloride (C-PVC) compound developed for the production of large-diameter industrial pressure pipes with outside diameters exceeding 600 mm. The compound is supplied in powder form and engineered to provide excellent heat resistance, long-term hydrostatic strength, superior processability, and outstanding dimensional stability during extrusion.
Its optimized formulation offers enhanced fusion characteristics, smooth melt flow, and excellent mechanical performance required for high-pressure industrial piping systems operating under demanding temperature and chemical exposure conditions. The deep grey color provides a professional industrial appearance while ensuring consistent color uniformity throughout production.
TG-C610A-G is particularly suitable for manufacturing heavy-duty C-PVC pressure pipes used in chemical processing plants, water treatment facilities, industrial fluid transportation systems, mining operations, and corrosive media handling applications.
Key Features
- Premium-grade C-PVC compound
- Designed for pressure pipes with OD ≥ 600 mm
- Excellent hydrostatic pressure resistance
- Superior heat resistance compared with conventional PVC compounds
- Outstanding chemical corrosion resistance
- Excellent fusion and processing stability
- High melt strength for large-diameter pipe extrusion
- Smooth internal and external pipe surface finish
- Low die build-up during processing
- Excellent dimensional stability
- Uniform deep grey coloration
- Long service life under elevated temperatures
- High impact strength and toughness
- Good weathering performance
- Reduced maintenance requirements
- Suitable for industrial and municipal infrastructure projects
Typical Applications
- High-pressure industrial piping systems
- Chemical transportation pipelines
- Water treatment facilities
- Industrial wastewater systems
- Desalination plants
- Mining slurry pipelines
- Process water pipelines
- Cooling water systems
- Corrosive fluid transportation
- Industrial utility piping
- Power plant piping systems
- Municipal infrastructure projects
- Large-diameter pressure pipe production
- Industrial process plants
- Petrochemical support systems
Technical Specification
| Property | Unit | Typical Value |
|---|---|---|
| Product Name | — | C-PVC Industrial Pipe Compound |
| Grade | — | TG-C610A-G |
| Appearance | — | Free-flowing Powder |
| Color | — | Deep Grey |
| Base Resin | — | Chlorinated Polyvinyl Chloride |
| Application | — | Industrial Pressure Pipe |
| Recommended Pipe OD | mm | ≥ 600 |
| Vicat Softening Temperature | °C | ≥ 110 |
| Tensile Strength | MPa | ≥ 50 |
| Impact Resistance | kJ/m² | ≥ 10 |
| Density | g/cm³ | 1.50 – 1.65 |
| Heat Stability (200°C) | min | ≥ 30 |
| Processing Temperature | °C | 185 – 210 |
| Melt Fusion Performance | — | Excellent |
| Surface Finish | — | Smooth |
| Dimensional Stability | — | Excellent |
| Chemical Resistance | — | Excellent |
| Pressure Resistance | — | High |
| Weather Resistance | — | Good |
| Extrusion Performance | — | Excellent |
| Moisture Content | % | ≤ 0.30 |
| Packaging | kg/bag | 25 |
Values shown are typical reference values and may be adjusted according to processing equipment and application requirements.
Processing Recommendations
| Parameter | Recommended Range |
|---|---|
| Material Drying Temperature | 70–80°C |
| Drying Time | 1–2 Hours |
| Barrel Temperature Zone 1 | 175–185°C |
| Barrel Temperature Zone 2 | 180–195°C |
| Barrel Temperature Zone 3 | 185–205°C |
| Die Temperature | 190–210°C |
| Screw Speed | According to pipe dimensions |
| Cooling Method | Vacuum Calibration + Water Cooling |
Advantages of EXTRUTEX TG-C610A-G
- Optimized for large-diameter pipe extrusion
- Consistent processing performance
- Excellent pressure-bearing capability
- Superior thermal resistance
- Long-term durability
- Excellent corrosion protection
- Reduced production downtime
- High production efficiency
- Uniform dispersion and fusion
- Reliable quality for industrial projects
Packaging & Storage
- Packed in 25 kg moisture-resistant bags.
- Store in a cool, dry, and well-ventilated area.
- Protect from direct sunlight and moisture.
- Keep packaging sealed until use.
- Recommended storage temperature below 35°C.
Features of OUR Ca/Zn Stabilizers
These stabilizers carry a quiet brilliance in their chemistry — qualities that make PVC behave not just well, but beautifully. Their strengths unfold like a list of promises:
• Excellent heat stability
They stand firm in the furnace of processing, guarding PVC against the harsh bite of thermal decay. Even under long residence times and high-output conditions, they keep the melt calm, steady, and true.
• Excellent processing
A formulation that flows like a well-rehearsed story — smooth, predictable, effortless. Machines run cleaner, extrusion runs longer, and operators breathe easier.
• High output rates
These stabilizers encourage speed. They let production lines surge forward, pushing greater volumes without sacrificing stability, gloss, or dimensional accuracy.
• Excellent plate-out properties
They keep the metal clean — die lips, barrels, calibrators — all free from waxy buildup. No residue, no streaks, no interruptions. Just pure, disciplined processing.
• Excellent dimensional stability
Pipes and fittings emerge with the confidence of perfect geometry. Sizes remain loyal to standards, resisting distortion, warpage, or shrinkage.
• Excellent surface finish
A stabilizer that leaves behind a sheen — a smooth, glasslike finish that speaks of controlled melt flow and refined lubrication balance.
APPLICATIONS:
-
(0 customer reviews)