EXTRUTEX C-PVC Compound for Industrial Pipe Grade: TG-C460A-G (Deep Grey Powder)
EXTRUTEX C-PVC Compound for Industrial Pipe
Grade: TG-C460A-G (Deep Grey Powder)
Technical Data Sheet
| Property | Unit | Typical Value |
|---|---|---|
| Product Name | — | C-PVC Industrial Pipe Compound |
| Grade | — | TG-C460A-G |
| Appearance | — | Free-flowing Powder |
| Color | — | Deep Grey |
| Base Polymer | — | Chlorinated Polyvinyl Chloride |
| Application | — | Industrial Pressure Pipe |
| Recommended Pipe OD | mm | 400 – 600 |
| Vicat Softening Temperature | °C | ≥ 110 |
| Tensile Strength | MPa | ≥ 48 |
| Impact Strength | kJ/m² | ≥ 9 |
| Density | g/cm³ | 1.50 – 1.65 |
| Heat Stability at 200°C | min | ≥ 30 |
| Processing Temperature | °C | 185 – 210 |
| Melt Flow Stability | — | Excellent |
| Surface Finish | — | Smooth |
| Pressure Resistance | — | High |
| Dimensional Stability | — | Excellent |
| Chemical Resistance | — | Excellent |
| Weather Resistance | — | Good |
| Extrusion Performance | — | Excellent |
| Moisture Content | % | ≤ 0.30 |
| Packaging | kg/bag | 25 |
EXTRUTEX C-PVC Compound for Industrial Pipe Grade: TG-C460A-G (Deep Grey Powder)
Description
EXTRUTEX C-PVC Compound for Industrial Pipe
Grade: TG-C460A-G (Deep Grey Powder)
Product Description
EXTRUTEX TG-C460A-G is a high-performance C-PVC (Chlorinated Polyvinyl Chloride) compound specially engineered for the extrusion of medium-to-large diameter industrial pressure pipes with outside diameters ranging from 400 mm to 600 mm. Supplied in deep grey powder form, this advanced compound delivers excellent thermal stability, superior hydrostatic strength, high rigidity, and outstanding processing consistency for demanding industrial applications.
The formulation is optimized to achieve smooth fusion behavior, stable melt flow, and excellent dimensional control during high-output extrusion processes. TG-C460A-G provides exceptional resistance against heat, corrosion, chemicals, and long-term pressure loading, making it highly suitable for industrial infrastructure and aggressive fluid handling systems.
Its premium-grade composition helps manufacturers produce high-quality pressure pipes with smooth surfaces, uniform wall thickness, excellent mechanical integrity, and long operational service life.
Main Features
- Premium-grade C-PVC industrial pipe compound
- Designed for pipe OD range: 400 mm – 600 mm
- Excellent hydrostatic pressure resistance
- Outstanding heat resistance
- Superior chemical and corrosion resistance
- Excellent extrusion process stability
- High melt strength for large-diameter pipe production
- Smooth internal and external pipe surfaces
- Excellent dimensional consistency
- Deep grey industrial color uniformity
- High mechanical strength and rigidity
- Long-term thermal aging resistance
- Good impact resistance
- Reduced die build-up during extrusion
- Stable production performance
- Suitable for high-output extrusion lines
Applications
- Industrial pressure pipe systems
- Chemical processing pipelines
- Industrial water supply systems
- Wastewater transportation systems
- Cooling water pipelines
- Desalination infrastructure
- Mining and slurry pipelines
- Corrosive fluid transportation
- Industrial utility piping
- Municipal infrastructure piping
- Power plant pipe systems
- Process water handling systems
- Heavy-duty industrial pipelines
- Large-diameter C-PVC pipes
- Industrial construction projects
Technical Specification Table
| Property | Unit | Typical Value |
|---|---|---|
| Product Name | — | C-PVC Industrial Pipe Compound |
| Grade | — | TG-C460A-G |
| Appearance | — | Free-flowing Powder |
| Color | — | Deep Grey |
| Base Polymer | — | Chlorinated Polyvinyl Chloride |
| Application | — | Industrial Pressure Pipe |
| Recommended Pipe OD | mm | 400 – 600 |
| Vicat Softening Temperature | °C | ≥ 110 |
| Tensile Strength | MPa | ≥ 48 |
| Impact Strength | kJ/m² | ≥ 9 |
| Density | g/cm³ | 1.50 – 1.65 |
| Heat Stability at 200°C | min | ≥ 30 |
| Processing Temperature | °C | 185 – 210 |
| Melt Flow Stability | — | Excellent |
| Surface Finish | — | Smooth |
| Pressure Resistance | — | High |
| Dimensional Stability | — | Excellent |
| Chemical Resistance | — | Excellent |
| Weather Resistance | — | Good |
| Extrusion Performance | — | Excellent |
| Moisture Content | % | ≤ 0.30 |
| Packaging | kg/bag | 25 |
The above values are typical reference data and may vary slightly according to processing conditions and equipment configuration.
Recommended Processing Parameters
| Parameter | Recommended Value |
|---|---|
| Material Drying Temperature | 70–80°C |
| Drying Time | 1–2 Hours |
| Barrel Zone 1 | 175–185°C |
| Barrel Zone 2 | 180–195°C |
| Barrel Zone 3 | 185–205°C |
| Die Temperature | 190–210°C |
| Screw Speed | Depending on pipe dimensions |
| Cooling System | Vacuum Calibration + Water Cooling |
Advantages of EXTRUTEX TG-C460A-G
- Optimized for medium and large industrial pressure pipes
- Excellent extrusion efficiency
- Superior long-term pressure durability
- High resistance to corrosive environments
- Stable melt rheology during extrusion
- Reduced processing defects
- Excellent pipe surface quality
- Reliable mechanical performance
- Long operational lifespan
- Suitable for demanding industrial applications
Packaging & Storage
- Packed in durable 25 kg moisture-proof bags.
- Store in dry, cool, and ventilated conditions.
- Avoid direct exposure to sunlight and humidity.
- Keep bags tightly sealed after opening.
- Recommended storage temperature below 35°C.
Features of OUR Ca/Zn Stabilizers
These stabilizers carry a quiet brilliance in their chemistry — qualities that make PVC behave not just well, but beautifully. Their strengths unfold like a list of promises:
• Excellent heat stability
They stand firm in the furnace of processing, guarding PVC against the harsh bite of thermal decay. Even under long residence times and high-output conditions, they keep the melt calm, steady, and true.
• Excellent processing
A formulation that flows like a well-rehearsed story — smooth, predictable, effortless. Machines run cleaner, extrusion runs longer, and operators breathe easier.
• High output rates
These stabilizers encourage speed. They let production lines surge forward, pushing greater volumes without sacrificing stability, gloss, or dimensional accuracy.
• Excellent plate-out properties
They keep the metal clean — die lips, barrels, calibrators — all free from waxy buildup. No residue, no streaks, no interruptions. Just pure, disciplined processing.
• Excellent dimensional stability
Pipes and fittings emerge with the confidence of perfect geometry. Sizes remain loyal to standards, resisting distortion, warpage, or shrinkage.
• Excellent surface finish
A stabilizer that leaves behind a sheen — a smooth, glasslike finish that speaks of controlled melt flow and refined lubrication balance.
APPLICATIONS:
Reviews (0)
Reviews
There are no reviews yet.
EXTRUTEX C-PVC Compound for Industrial Pipe
Grade: TG-C460A-G (Deep Grey Powder)
Product Description
EXTRUTEX TG-C460A-G is a high-performance C-PVC (Chlorinated Polyvinyl Chloride) compound specially engineered for the extrusion of medium-to-large diameter industrial pressure pipes with outside diameters ranging from 400 mm to 600 mm. Supplied in deep grey powder form, this advanced compound delivers excellent thermal stability, superior hydrostatic strength, high rigidity, and outstanding processing consistency for demanding industrial applications.
The formulation is optimized to achieve smooth fusion behavior, stable melt flow, and excellent dimensional control during high-output extrusion processes. TG-C460A-G provides exceptional resistance against heat, corrosion, chemicals, and long-term pressure loading, making it highly suitable for industrial infrastructure and aggressive fluid handling systems.
Its premium-grade composition helps manufacturers produce high-quality pressure pipes with smooth surfaces, uniform wall thickness, excellent mechanical integrity, and long operational service life.
Main Features
- Premium-grade C-PVC industrial pipe compound
- Designed for pipe OD range: 400 mm – 600 mm
- Excellent hydrostatic pressure resistance
- Outstanding heat resistance
- Superior chemical and corrosion resistance
- Excellent extrusion process stability
- High melt strength for large-diameter pipe production
- Smooth internal and external pipe surfaces
- Excellent dimensional consistency
- Deep grey industrial color uniformity
- High mechanical strength and rigidity
- Long-term thermal aging resistance
- Good impact resistance
- Reduced die build-up during extrusion
- Stable production performance
- Suitable for high-output extrusion lines
Applications
- Industrial pressure pipe systems
- Chemical processing pipelines
- Industrial water supply systems
- Wastewater transportation systems
- Cooling water pipelines
- Desalination infrastructure
- Mining and slurry pipelines
- Corrosive fluid transportation
- Industrial utility piping
- Municipal infrastructure piping
- Power plant pipe systems
- Process water handling systems
- Heavy-duty industrial pipelines
- Large-diameter C-PVC pipes
- Industrial construction projects
Technical Specification Table
| Property | Unit | Typical Value |
|---|---|---|
| Product Name | — | C-PVC Industrial Pipe Compound |
| Grade | — | TG-C460A-G |
| Appearance | — | Free-flowing Powder |
| Color | — | Deep Grey |
| Base Polymer | — | Chlorinated Polyvinyl Chloride |
| Application | — | Industrial Pressure Pipe |
| Recommended Pipe OD | mm | 400 – 600 |
| Vicat Softening Temperature | °C | ≥ 110 |
| Tensile Strength | MPa | ≥ 48 |
| Impact Strength | kJ/m² | ≥ 9 |
| Density | g/cm³ | 1.50 – 1.65 |
| Heat Stability at 200°C | min | ≥ 30 |
| Processing Temperature | °C | 185 – 210 |
| Melt Flow Stability | — | Excellent |
| Surface Finish | — | Smooth |
| Pressure Resistance | — | High |
| Dimensional Stability | — | Excellent |
| Chemical Resistance | — | Excellent |
| Weather Resistance | — | Good |
| Extrusion Performance | — | Excellent |
| Moisture Content | % | ≤ 0.30 |
| Packaging | kg/bag | 25 |
The above values are typical reference data and may vary slightly according to processing conditions and equipment configuration.
Recommended Processing Parameters
| Parameter | Recommended Value |
|---|---|
| Material Drying Temperature | 70–80°C |
| Drying Time | 1–2 Hours |
| Barrel Zone 1 | 175–185°C |
| Barrel Zone 2 | 180–195°C |
| Barrel Zone 3 | 185–205°C |
| Die Temperature | 190–210°C |
| Screw Speed | Depending on pipe dimensions |
| Cooling System | Vacuum Calibration + Water Cooling |
Advantages of EXTRUTEX TG-C460A-G
- Optimized for medium and large industrial pressure pipes
- Excellent extrusion efficiency
- Superior long-term pressure durability
- High resistance to corrosive environments
- Stable melt rheology during extrusion
- Reduced processing defects
- Excellent pipe surface quality
- Reliable mechanical performance
- Long operational lifespan
- Suitable for demanding industrial applications
Packaging & Storage
- Packed in durable 25 kg moisture-proof bags.
- Store in dry, cool, and ventilated conditions.
- Avoid direct exposure to sunlight and humidity.
- Keep bags tightly sealed after opening.
- Recommended storage temperature below 35°C.
Features of OUR Ca/Zn Stabilizers
These stabilizers carry a quiet brilliance in their chemistry — qualities that make PVC behave not just well, but beautifully. Their strengths unfold like a list of promises:
• Excellent heat stability
They stand firm in the furnace of processing, guarding PVC against the harsh bite of thermal decay. Even under long residence times and high-output conditions, they keep the melt calm, steady, and true.
• Excellent processing
A formulation that flows like a well-rehearsed story — smooth, predictable, effortless. Machines run cleaner, extrusion runs longer, and operators breathe easier.
• High output rates
These stabilizers encourage speed. They let production lines surge forward, pushing greater volumes without sacrificing stability, gloss, or dimensional accuracy.
• Excellent plate-out properties
They keep the metal clean — die lips, barrels, calibrators — all free from waxy buildup. No residue, no streaks, no interruptions. Just pure, disciplined processing.
• Excellent dimensional stability
Pipes and fittings emerge with the confidence of perfect geometry. Sizes remain loyal to standards, resisting distortion, warpage, or shrinkage.
• Excellent surface finish
A stabilizer that leaves behind a sheen — a smooth, glasslike finish that speaks of controlled melt flow and refined lubrication balance.